Weicon Anti-Seize Nickel Assembly Paste, 26050100, 1 Kg

The assembly paste was developed to resist extreme conditions. It is highly sticky, water repellent and resistant to sweet, salt and hot water as well as steam. The high nickel component furthermore provides protection against corroding and corrosive solvents which are contained in diluted hydrochloric acid, sulphur or nitric acid, among others. Anti-Seize Nickel can be applied at a large temperature range between -30 Deg.C to 1450 Deg.C. Anti-Seize Nickel serves as corrosion protection and high performance fitting grease for static and dynamically extremely stressed screw connections and installation parts and the application at slowly rotating system in the high-temperature range. The paste protects against corrosion, seizing, wear, stick-slip effects, oxidation and friction corrosion as well as electrolytic reactions, the so-called cold-sealing. For example, Anti-Seize Nickel can be used on seals, valves, screw connections, gear wheels, bearings, jets, conveyor belts, studs, tools or cylinders.
Surface pre-treatment

Clean and degrease surfaces. Apply the assembly paste evenly. AS is suitable only for assembly paste specific applications, it does not replace pure lubricants and greases.

Processing

Apply a good quantity of Assembly Paste with a brush, cloth or plastic sponge. On threads it is important that Assembly Paste is applied down to the thread root to ensure a good sealing effect. Assembly Paste must not be mixed with greases or oils to avoid changes in the material characteristics. Weicon Assembly Pastes do not replace oil or grease lubrication.

Technical Data:

Basic Oil: Synthetic Oil

Colour: Anthracite

Density at +20 Deg.C (+68 Deg.F) (DIN 51757): 1.3 g/cu.cm

OFW device coefficient of friction: 0.16

Friction total: 0.15 µ

Friction thread: 0.14 µ

Friction head bottom: 0.16 µ

VKA-TEST (DIN 51350) welding load: 2000 N

VKA-TEST (DIN 51350) Spherical cap value (1Min/1000N): 0.6mm

Worked penetration ( DIN ISO 2137): 310 - 340 1/10mm

Specific heat transfer capacity (20 Deg.C): 1493 J/(g·K)

Thermal diffusivity (20 Deg.C): 0.303 sq.mm/s

Thermal conductivity (ISO 22007-4) (20 Deg.C): 0.582 W/m·K

Dielectric strength (DIN EN 60243-1) (20 Deg.C): 1.1 kV/mm

Sulfur content (DIN 514): <0.1%

Water resistance (DIN 51807): 1 - 90

Pressure (DIN 53281-83): 230 N/sq.mm

Salt spray test: >170 h

Temperature Resistance: -30 to 1.450 Deg.C